ΑΝΑΠΤΥΞΗ ΤΗΣ ΠΟΡΩΔΟΥΣ ΔΟΜΗΣ ΛΙΓΝΙΤΩΝ ΚΑΤΑ ΤΗΝ ΕΞΑΕΡΙΩΣΗ ΤΟΥΣ

Περίληψη

THE DEVELOPMENT OF PORE SURFACE AREA, VOLUME AND SIZE DISTRIBUTION DURING LIGNITE HYDROGASIFICATION IS ANALYZED IN THE PRESENT THESIS. REACTION TIME AND TEMPERATURE ARE CORRELATED WITH PORE PARAMETERES VARIATION. THE INFLUENCE OF THREE CATALYSTS K2CO3, KOH, K-ZN IS ALSO DETECTED. FOR THE ABOVE CONDITIONS, THE KINETIC CONSTANTS AND ACTIVATION ENERGIES ARE CALCULATED AS WELL AS THE SPECIFIC HYDROGASIFICATION RATES. FINALLY THE BHATHIA-PERLMUTTER THEORETICAL MODELFOR THE PRODUCTION OF SURFACE AREA VARIATION IS APPLIED ON THE EXPERIMENTAL RESULTS. MICRO AND MESOPORE CHARACTERISTICS ARE OBTAINED WITH THE USE OF ADSORPTION OF CO2 AT 298K AT N2 AND 77K RESPECTIVELY. RESULTS SHOW AN INCREASE OF MICROPOROSITY DURING THE INITIAL HYDROPYROLYSIS STEP AND LATTER AND INCREASE IN MESOPOROSITY, DURING HYDROGASIFICATION STEP. ALL CATALYSTS TESTED ARE CAUSING A CONSIDERABLE INCREASE IN PORE STRUCTURE CHARACTERISTICS. THIS UNUSUAL BEHAVIOR IS ATTRIBUTED TO THE PRODUCT SELECTIVITY. F ...
περισσότερα
Πρέπει να είστε εγγεγραμένος χρήστης για έχετε πρόσβαση σε όλες τις υπηρεσίες του ΕΑΔΔ  Είσοδος /Εγγραφή

Όλα τα τεκμήρια στο ΕΑΔΔ προστατεύονται από πνευματικά δικαιώματα.

DOI
10.12681/eadd/3179
Διεύθυνση Handle
http://hdl.handle.net/10442/hedi/3179
Εναλλακτικός τίτλος
PORE STRUCTURE DEVELOPMENT IN LIGNITE GASIFICATION
Συγγραφέας
ΣΤΑΥΡΟΠΟΥΛΟΣ, ΓΕΩΡΓΙΟΣ
Ημερομηνία
1994
Ίδρυμα
Αριστοτέλειο Πανεπιστήμιο Θεσσαλονίκης (ΑΠΘ). Σχολή Πολυτεχνική. Τμήμα Χημικών Μηχανικών
Εξεταστική επιτροπή
ΣΑΚΕΛΛΑΡΟΠΟΥΛΟΣ ΓΕΩΡΓΙΟΣ
ΒΑΣΑΛΟΣ ΙΑΚΩΒΟΣ
ΚΑΡΑΜΠΕΛΑΣ ΑΝΑΣΤΑΣΙΟΣ
ΠΛΑΤΑΚΗΣ ΝΙΚΟΛΑΟΣ
ΑΝΔΡΟΥΤΣΟΠΟΥΛΟΣ ΓΕΩΡΓΙΟΣ
Επιστημονικό πεδίο
Μηχανική & Τεχνολογία
Επιστήμες Χημικού Μηχανικού
Λέξεις-κλειδιά
ΕΙΔΙΚΗ ΕΠΙΦΑΝΕΙΑ; ΕΞΑΕΡΙΩΣΗ; Λιγνίτες; Πορώδης δομή
Χώρα
Ελλάδα
Γλώσσα
Ελληνικά