Abstract

VARIΟUS MODIFIED POLYMERS SUCH AS POLYIMIDES, POLYMIDES, POLYESTERS, POLYURETHANES AND EPOXY RESINS WERE SYNTHESIZED AND CHARACTERIZED. THEIR CHEMICAL, PHYSICAL AND THERMAL PROPERTIES WERE INVESTIGATED AND COMPARED WITH THOSE OF THE CORRESPONDING UNMODIFIED POLYMERS. THE MODIFICATION OF POLYMERS INCREASED SIGNIFICANTLY THEIR SOLUBILITY IN COMMON ORGANIC SOLVENTS AS WELL AS THEIR THERMAL STABILITY. SOME OF THE SYNTHESIZED POLYMERS BEARING OLEFINIC BONDS AND/OR CYANO GROUPS YIELDED BY HEAT-CURING THERMALLY STABLE CROSSLINKED POLYMERS WITHOUT EVOLUTION OF VOLATILE BYPRODUCTS. THEY COULD DE USED AS MATRIX RESINS FOR HIGH TEMPERATURE COMPOSITES BEING STABLE UP TO 300-450 C AND AFFORDING ANAEROBIC CHAR YIELDS OF 54-84% AT 800 C. IN ADDITION, SOME CONDUCTIVE MATERIALS HAVING ELECTRICAL CONDUCTIVITY 4-20 S CM-1 AT 27 C WERE PREPARED BY PYROLYSING UNSATURATED CYANOSUBSTITUTED POLYMER PRECURSORS.

ΣΥΝΕΤΕΘΗΚΑΝ ΔΙΑΦΟΡΑ ΤΡΟΠΟΠΟΙΗΜΕΝΑ ΠΟΛΥΜΕΡΗ, ΟΠΩΣ ΠΟΛΥΑΜΙΔΙΑ, ΠΟΛΥΙΜΙΔΙΑ, ΠΟΛΥΕΣΤΕΡΕΣ, ΠΟΛΥΟΥΡΕΘΑΝΕΣ ΚΑΙ ΕΠΟΞΕΙΔΙΚΕΣ ΡΗΤΙΝΕΣ. ΟΙ ΧΗΜΙΚΕΣ, ΦΥΣΙΚΕΣ ΚΑΙ ΘΕΡΜΙΚΕΣ ΙΔΙΟΤΗΤΕΣ ΑΥΤΩΝ ΕΡΕΥΝΗΘΗΚΑΝ ΚΑΙ ΣΥΓΚΡΙΘΗΚΑΝ ΜΕ ΕΚΕΙΝΕΣ ΤΩΝ ΑΝΤΙΣΤΟΙΧΩΝ ΜΗ ΤΡΟΠΟΠΟΙΗΜΕΝΩΝ ΠΟΛΥΜΕΡΩΝ. Η ΤΡΟΠΟΠΟΙΗΣΗ ΤΩΝ ΠΟΛΥΜΕΡΩΝ ΑΥΞΗΣΕ ΣΗΜΑΝΤΙΚΑ ΤΗ ΔΙΑΛΥΤΟΤΗΤΑ ΑΥΤΩΝ ΣΕ ΣΥΝΗΘΕΙΣ ΟΡΓΑΝΙΚΟΥΣ ΔΙΑΛΥΤΕΣ ΚΑΘΩΣ ΚΑΙ ΤΗ ΘΕΡΜΙΚΗ ΤΟΥΣ ΣΤΑΘΕΡΟΤΗΤΑ. ΟΡΙΣΜΕΝΑ ΑΠΟ ΤΑ ΠΟΛΥΜΕΡΗ ΠΟΥ ΣΥΝΕΤΕΘΗΣΑΝ, ΤΑ ΟΠΟΙΑ ΠΕΡΙΕΙΧΑΝ ΟΛΕΦΙΝΙΚΟΥΣ ΔΕΣΜΟΥΣ Η/ΚΑΙ ΚΥΑΝΟ ΟΜΑΔΕΣ, ΕΔΩΣΑΝ ΜΕ ΘΕΡΜΙΚΗ ΕΠΕΞΕΡΓΑΣΙΑ ΘΕΡΜΟΑΝΘΕΚΤΙΚΑ ΔΙΑΣΥΝΔΕΔΕΜΕΝΑ ΠΟΛΥΜΕΡΗ ΧΩΡΙΣ ΤΗΝ ΕΚΛΥΣΗ ΠΤΗΤΙΚΩΝ ΠΑΡΑΠΡΟΙΟΝΤΩΝ. ΑΥΤΑ ΘΑ ΜΠΟΡΟΥΣΑΝ ΝΑ ΧΡΗΣΙΜΟΠΟΙΗΘΟΥΝ ΩΣ ΥΠΟΣΤΡΩΜΑ ΣΕ ΣΥΝΘΕΤΑ ΥΛΙΚΑ ΥΨΗΛΩΝ ΘΕΡΜΟΚΡΑΣΙΩΝ, ΕΠΕΙΔΗ ΗΤΑΝ ΣΤΑΘΕΡΑ ΜΕΧΡΙ ΤΟΥΣ 300-400 ΒΑΘΜΟΥΣ ΚΕΛΣΙΟΥ ΚΑΙ ΣΧΗΜΑΤΙΣΑΝ ΑΝΑΕΡΟΒΙΟ ΑΠΑΝΘΡΑΚΩΜΑ 54-84% ΣΤΟΥΣ 800 ΒΑΘΜΟΥΣ ΚΕΛΣΙΟΥ. ΠΑΡΑΣΚΕΥΑΣΤΗΚΑΝ ΕΠΙΣΗΣ ΑΓΩΓΙΜΑ ΥΛΙΚΑ ΠΟΥ ΕΙΧΑΝ ΗΛΕΚΤΡΙΚΗ ΑΓΩΓΙΜΟΤΗΤΑ 4-20 S CM-1 ΣΤΟΥΣ 27 ΒΑΘΜΟΥΣ ΔΙΑ ΠΥΡΟΛΥΣΕΩΣ ΟΡΙΣΜΕΝΩΝ ΑΚΟΡΕΣΤΩΝ ΚΥΑΝΟ-ΥΠΟΚΑΤΕΣΤΗΜΕΝΩΝ Η ΠΡΟΔΡΟΜΩΝ ΠΟΛΥΜΕΡΩΝ.