Πειραματική μελέτη διερεύνησης νευροτοξικότητας συνθετικών νανοϋλικών

Abstract

There is an increasing number of novel technologies that are proposed for biomedical use. Besides their efficiency, new technologies are controlled for their safety. The goal of the present thesis is not assess potential neurotoxicity of synthetic nanomaterials, with an emphasis on the use of Pathology. For this study two types of nanoparticles were selected. Both were made of PLGA, one with chitosan coating and the other without. Potential neurotoxicity was evaluated both in vitro and in vivo, with testing on wistar rats. The results from the testing showed that PLGA nanoparticles with chitosan coating do not show neurotoxicity and have superior performance compared to those without chitosan coating.

Ολοένα και αυξάνει ο αριθμός των καινοτόμων τεχνολογιών που προτείνονται για χρήση σε βιοϊατρικές εφαρμογές. Πέρα από την αποτελεσματικότητά τους, οι νέες τεχνολογίες ελέγχονται και για την ασφάλειά τους. Σκοπός της παρούσας διατριβής είναι η διερεύνηση κατά πόσον συνθετικά νανοϋλικά έχουν νευροτοξική δράση, με έμφαση στην χρήση τεχνικών Παθολογικής Ανατομικής στην Ιατρική. Προς μελέτη επιλέχθηκαν δύο τύποι νανοσωματιδίων: αμφότεροι τύποι είχαν ως υλικό κατασκευή το πολυμερές PLGA, ο ένας τύπος με συμπερίληψη κελύφους χιτοζάνης ενώ ο έτερος χωρίς. Η πιθανή νευροτοξικότητα ελέγχθηκε τόσο in vitro όσο και in vivo με πειραματισμό σε επίμυες. Τα αποτελέσματα του πειραματικού ελέγχου έδειξαν πως τα PLGA νανοσωματίδια με κέλυφος χιτοζάνης δεν εμφανίζουν νευροτοξικότητα και υπερέχουν σημαντικά σε σχέση με τα νανοσωματίδια χωρίς κέλυφος χιτοζάνης.